Three-phase firing (or three-step firing) or iron reduction technique is a firing technique used in ancient Greek pottery production, specifically for painted vases. Already vessels from the Bronze Age feature the colouring typical of the technique, with yellow, orange or red clay and brown or red decoration. By the 7th century BC, the process was perfected in mainland Greece (Corinth and Athens) enabling the production of extremely shiny black-slipped surfaces, which led to the development of the black-figure and red-figure techniques, which dominated Greek vase painting until about 300 BC.
| Attributes | Values |
|---|
| rdf:type
| |
| rdfs:label
| - Dreiphasenbrand (de)
- Three-phase firing (en)
- Технология изготовления и декорирования древнегреческой керамики (ru)
- Технологія виготовлення та декорування давньогрецької кераміки (uk)
|
| rdfs:comment
| - Als Dreiphasenbrand, (auch: Dreistufenbrand), wird ein Brennverfahren in der Keramikproduktion des antiken Griechenland bezeichnet. Schon bronzezeitliche Gefäße weisen die für dieses Verfahren typische Dreifarbigkeit (Tongrund gelblich bis orange-rot o. ä., Dekor braun-rot und schwarz) auf. Etwa im 7. Jahrhundert v. Chr. wurde das Verfahren in Griechenland perfektioniert, so dass nun hochglänzende schwarze Oberflächen möglich wurden, und bis um 300 v. Chr. zur Herstellung schwarzfiguriger und rotfiguriger Vasen eingesetzt. (de)
- Three-phase firing (or three-step firing) or iron reduction technique is a firing technique used in ancient Greek pottery production, specifically for painted vases. Already vessels from the Bronze Age feature the colouring typical of the technique, with yellow, orange or red clay and brown or red decoration. By the 7th century BC, the process was perfected in mainland Greece (Corinth and Athens) enabling the production of extremely shiny black-slipped surfaces, which led to the development of the black-figure and red-figure techniques, which dominated Greek vase painting until about 300 BC. (en)
- Технология изготовления и декорирования древнегреческой керамики всегда интересовала не только археологов, историков искусства, но и представителей точных наук. Впервые все этапы изготовления керамики Древней Греции рассмотрела в 1923 году американская исследовательница Жизель Рихтер в работе The craft of Athenian pottery. Следующим важным этапом на пути познания технологии создания древнегреческой керамики стали исследования немецкого археолога Теодора Шумана, который сумел установить состав чёрного лака (см. Чернолаковая керамика). В послевоенное время появился ряд публикаций об отдельных стадиях и приемах производства аттической керамики. Среди них и поныне наибольшую ценность представляют работы британского археолога Джона Дэвидсона Бизли Potters and Painters in Ancient Athens 1944 год (ru)
- Технологія виготовлення та декорування давньогрецької кераміки завжди цікавила не тільки археологів, істориків мистецтва, але й представників точних наук. Вперше усі етапи виготовлення кераміки Стародавньої Греції розглянула 1923 року американська дослідниця у праці «The craft of Athenian pottery». Наступним важливим етапом на шляху пізнання технології виробництва давньогрецької кераміки стали дослідження німецького археолога Теодора Шумана, який зумів встановити склад чорного лаку (див. Чорнолакова кераміка). У післявоєнний час з'явилась низка публікацій про окремі стадії та прийоми виробництва аттичної кераміки. Серед них і донині найбільшу цінність являють праці британського археолога Джона Бізлі «Potters and Painters in Ancient Athens» 1944 року, а також Джозефа Ноубля «The Techniques (uk)
|
| foaf:depiction
| |
| dcterms:subject
| |
| Wikipage page ID
| |
| Wikipage revision ID
| |
| Link from a Wikipage to another Wikipage
| |
| sameAs
| |
| dbp:wikiPageUsesTemplate
| |
| thumbnail
| |
| has abstract
| - Als Dreiphasenbrand, (auch: Dreistufenbrand), wird ein Brennverfahren in der Keramikproduktion des antiken Griechenland bezeichnet. Schon bronzezeitliche Gefäße weisen die für dieses Verfahren typische Dreifarbigkeit (Tongrund gelblich bis orange-rot o. ä., Dekor braun-rot und schwarz) auf. Etwa im 7. Jahrhundert v. Chr. wurde das Verfahren in Griechenland perfektioniert, so dass nun hochglänzende schwarze Oberflächen möglich wurden, und bis um 300 v. Chr. zur Herstellung schwarzfiguriger und rotfiguriger Vasen eingesetzt. (de)
- Three-phase firing (or three-step firing) or iron reduction technique is a firing technique used in ancient Greek pottery production, specifically for painted vases. Already vessels from the Bronze Age feature the colouring typical of the technique, with yellow, orange or red clay and brown or red decoration. By the 7th century BC, the process was perfected in mainland Greece (Corinth and Athens) enabling the production of extremely shiny black-slipped surfaces, which led to the development of the black-figure and red-figure techniques, which dominated Greek vase painting until about 300 BC. The conventional view, developed in modern times in view of a lack of contemporary accounts, was that painted Greek pottery received a single firing, after the shaped pot had been dried leather-hard and then painted. But the firing had three phases, designed to create the intended colours. Sometimes further painting in other colours was added after firing, especially in white-ground and Hellenistic vases. However, new studies instead provide material evidence that the pottery was made with two or more separate firings in which the pottery is subjected to multiple firing stages. The conventional view is described in more detail below, but the possibility of different firings for the phases described should be kept in mind. (en)
- Технология изготовления и декорирования древнегреческой керамики всегда интересовала не только археологов, историков искусства, но и представителей точных наук. Впервые все этапы изготовления керамики Древней Греции рассмотрела в 1923 году американская исследовательница Жизель Рихтер в работе The craft of Athenian pottery. Следующим важным этапом на пути познания технологии создания древнегреческой керамики стали исследования немецкого археолога Теодора Шумана, который сумел установить состав чёрного лака (см. Чернолаковая керамика). В послевоенное время появился ряд публикаций об отдельных стадиях и приемах производства аттической керамики. Среди них и поныне наибольшую ценность представляют работы британского археолога Джона Дэвидсона Бизли Potters and Painters in Ancient Athens 1944 года, а также Джозефа Ноубла The Techniques of Painted Attic Pottery. Любопытно вот что — на некоторых сосудах есть красные фигуры, черные фигуры, а также белый ангоб и добавленый рисунок поверх чёрной или красной глазури, сделанный кремового цвета глиной. Отчасти в керамике сохранились остатки углерода в виде тонкой темной полосы лежащей непосредственно под глазурью. Из выше сказанного можно сделать вывод о том что все 4 цвета наносились последовательно и до однократного обжига. (ru)
- Технологія виготовлення та декорування давньогрецької кераміки завжди цікавила не тільки археологів, істориків мистецтва, але й представників точних наук. Вперше усі етапи виготовлення кераміки Стародавньої Греції розглянула 1923 року американська дослідниця у праці «The craft of Athenian pottery». Наступним важливим етапом на шляху пізнання технології виробництва давньогрецької кераміки стали дослідження німецького археолога Теодора Шумана, який зумів встановити склад чорного лаку (див. Чорнолакова кераміка). У післявоєнний час з'явилась низка публікацій про окремі стадії та прийоми виробництва аттичної кераміки. Серед них і донині найбільшу цінність являють праці британського археолога Джона Бізлі «Potters and Painters in Ancient Athens» 1944 року, а також Джозефа Ноубля «The Techniques of Painted Attic Pottery». (uk)
|
| gold:hypernym
| |
| prov:wasDerivedFrom
| |
| page length (characters) of wiki page
| |
| foaf:isPrimaryTopicOf
| |
| is Link from a Wikipage to another Wikipage
of | |
| is foaf:primaryTopic
of | |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)